Deze tekst presenteert het gegevensblad van Rogers 4350b, en geef vervolgens enkele verklaringen voor de belangrijke gegevens en de kenmerken ervan. Ook, we explore the adaption of 4350b rogers towards PCB mass production at the end, with its further application.
Eigendom | Waarde | Eenheden | Direction |
Diëlektrische constante,e, Werkwijze | 3.48 | / | MET |
Diëlektrische constante,e, Ontwerp | 3.66 | / | MET |
Dissipatiefactor tan,d | 0.0037 0.0031 | / | MET |
Thermal Coefficient of e, | +50 | Ppm/℃ | MET |
Volumeweerstand | 1.2*10^10 | MΩ*cm | / |
Oppervlakte weerstand | 5.7*10^9 | MΩ | / |
Elektrische sterkte | 3.12(780) | KV / mm(V / mil) | MET |
Trekmodulus | 16767(2432) 14153(2053) | MPa(ksi) | X EN |
Treksterkte | 203(29.5) 130(18.9) | MPa(ksi) | X EN |
Buigsterkte | 255(37) | MPa(kpsi) | / |
Dimensionale stabiliteit | <0.5 | Mm/m(mils/inch) | X, EN |
Coefficient Thermal Expansion | 10 12 32 | Ppm/℃ | X EN MET |
Tg | >280 | ℃ TMA | / |
Td | 390 | ℃ TGA | / |
Warmtegeleiding | 0.69 | W / m / ° K | / |
Vochtopname | 0.06 | % | / |
Dichtheid | 1.86 | G/cm³ | / |
Copper Peel Strength | 0.88(5.0) | N/mm(pli) | / |
Ontvlambaarheid | V-0 | / | / |
Lead-Free Process Compatible | Ja | / | / |
Tg>280 indicates that the glass transition temperature is 280 centigrade. Met andere woorden, when the temperature reaches 280 centigrade, Ro4350b begins to change from a highly elastic state to a glassy state. This transformation process is the macroscopic embodiment of polymer motion form transmission, which will directly affect the its performance and original properties.
Td>340 means thermal decomposition temperature is above 390 centigrade. Dat is, when 4350b rogers reaches 340 centigrade, the bonds inside its molecules begin to break, creating a new chemical reaction. Its physical properties makes related change, te.
4350b rogers has a dielectric constant of 3.48, which is lower than the data of fr4 commonly used in the PCB industry. This means that it has a lower propagation speed of electromagnetic waves. This further helps to reduce the delay of signal transmission and improve the speed and efficiency of signal transmission.
Ondertussen, its dielectric constant tolerance is relatively low. Met andere woorden, its range of dielectric constant variation is small. Low dielectric constant tolerance greatly contributes to good micro-structure of the material. Daarom, the defects and impurities inside the material are less, leading to stable performance of the dielectric material. All these factors have a positive effect on the behavior of the dielectric in the electric field as well as the dielectric loss, causing less energy loss. Daarnaast, its low dielectric constant temperature fluctuation is low. This allows reduction of PCB signal delay and distortion due to temperature changes, for improving the reliability and stability of the device.
Ro4350b coefficient thermal expansion at Z-axis is as low as 32 ppm/℃. When the temperature changes, the material expands or contracts less in the z-axis (usually the direction perpendicular to the plane or surface). This helps to maintain the stability of the PCB structure. Tweede, the low Z-axis thermal expansion coefficient reduce thermal stress, preventing stress accumulation and damage within the PCB due to temperature fluctuation. Verder, since the size of the material are less affected by temperature changes, designer can set the PCB structure in a more flexibly way without extra compensation measures for thermal expansion. Ook, this reduces costs and enhance production efficiency.
When the printed board is working, especially under the condition where there is ion pollution and certain humidity, the metal between the adjacent wires or metallization holes may dissolve into ions and then precipitate in the insulation layer and surface, thereby reducing the insulation resistance of the material. alternatief, conductive ions migrate inside the material along the glass fibers.
Then CAF impedance of rogers ro4350b is an excellent solution to the above problems. Its insulation performance so good that it can prevent current leakage and short circuit. A reducing equipment damage and repair costs due to electrical failures. Ook, CAF impedance is critical for high-speed electronic devices and high-frequency signals equipment. It can improve the transmission efficiency of the circuit board and reduce the signal loss. Tenslotte, CAF impedance is capable of preventing PCB fire or equipment damage due to current overload.
4350b rogers high-frequency board is fully adaptable to traditional PCB manufacturing techniques without special pre-treatment for through-hole copper plating (plasma treatment for PTFE plates) or any other extra processes. During solder resistance process, it can also adapts grind the board. Bovendien, compared to traditional microwave material laminates, they are cheaper, so they are widely used in high-power RF design required fire protection class UL 94V-0. Met name, its processing technology is similar to FR-4, so it is suitable for batch producing as well as pressing with FR4 together for multiple PCB.
Thanks to its excellent dielectric constant, coefficient thermal expansion and CAF impedance, it is gains popularity in the field of high-frequency telecom field. Bijvoorbeeld, it is widely applied for cellular base station antennas, power amplifiers, microwave point-to-point connections, automotive radars and sensors, radio frequency identification tags, and high frequency heads for live broadcasting satellites.
In the world of printed circuit board design and manufacturing, precision and accuracy are paramount.…
Soldering is a cornerstone technique in electronics assembly, it's used to connect electrical pieces and…
Vandaag de dag, electronic products are both compact and lightweight while performing a variety of functions. Dit…
As technology continues to advance in the electronics industry, packaging remains one of the key…
Bringing your electronic ideas to life begins with PCB drawing, which is the process of…
Printed Circuit Board design is one of the most significant processes in electronics production. Deciding…